crazing

英

美

n.  银纹；破裂；龟裂；细裂纹

电力

双语例句

• The control and prevention measure i.e.to reduce mental material tensile stress, select suitable material, control of media environment and scheduled maintenance to the pipe is put forward aimed to stress corrosion crazing problem produced by stainless steel welded pipe for condenser.
  针对凝汽器用不锈钢焊管产生应力腐蚀开裂问题提出了抑制和防范措施，即降低金属材料拉伸应力，选择合适的材料，对介质环境的控制和对钢管的定期维护保养。
• Crazing resistance of glazed ceramic whiteware by a thermal shock method cold crack temperature
  陶瓷砖釉面抗龟裂试验方法：抗热震性法低温龟裂温度，冷裂温度
• Crazing Toughening Design of Brittle Polymer Solids
  脆性高聚物的银纹化增韧设计
• Research on Time-Temperature-Stress Superposition Principle of PMMA's Crazing Damage
  PMMA银纹损伤时温应力等效研究
• Secondly, a new concept& crazing variable is defined base on the damage variable and the toughening equation set up by the fractal dimension of crazes, which allows the two important properties of crazing: damage and toughening.
  其次，在利用分形维数建立的损伤变量和韧化函数的基础上，定义了一个全新的概念：银纹变量。它可以表征银纹损伤和银纹增韧对材料的共同作用。
• The ratio of the crazing to the shear ribbon was analysed by WAXS.
  采用光散射法（WAXS）分析银纹和剪切带比例。
• Great energy must be consumed during craze initiation, growth and fracture, thus crazing is very important for polymer toughening design.
  银纹在其引发、生长和断裂过程中消耗大量能量，对高聚物的增韧设计十分重要。
• An optical technique to quantify the creep crazing damage in stressed transparent glassy polymeric sheet of PMMA is presented.
  采用光学显微技术对高聚物蠕变条件下的银纹损伤引发和演化进行了实验观测。
• This paper states the causes and prevention measure of longitudinal crazing of joints of pre-cast floor slab from the aspects of design, construction and material.
  本文从设计、施工、材料等方面论述了预制楼板板缝纵向开裂产生原因及防治措施。
• Higher temperature can make paint's surface crazing and bubbling; while lower can cause it difficult to solidify and appear flowing phenomenon.
  温度过高会导致漆膜开裂、起泡；温度过低使漆膜不易固化，出现流挂现象。